Samsung Cheil Industries Infino: WP-1041G;WP-1069,WP-1089;WP-1098;
| Samsung Cheil Industries Infino? WP-1069 PC/ABS, Unreinforced | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; ABS Polymer; Polycarbonate/ABS Alloy, Unreinforced; Polycarbonate (PC) | ||
| Material Notes: |
Information provided by Samsung Cheil Industries. |
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow |
0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow |
47 g/10 min @Load 10.0 kg, Temperature 250 °C |
47 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength at Break | 54.9 MPa | 7960 psi | ASTM D638 |
| Tensile Strength, Yield | 53.0 MPa | 7680 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 87 % | 87 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.01 GPa | 292 ksi | ASTM D638 |
| Flexural Strength | 78.5 MPa | 11400 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.21 GPa | 320 ksi | 2.8 mm/min; ASTM D638 |
Izod Impact, Notched 
|
1.96 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
3.67 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 |
|
3.92 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
7.35 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 | |
|
4.22 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
7.90 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
|
5.69 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
10.7 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow |
8.20 μm/m-°C @Temperature 40.0 - 100 °C |
4.56 μin/in-°F @Temperature 104 - 212 °F |
ASTM E831 |
| CTE, linear, Transverse to Flow |
8.30 μm/m-°C @Temperature 40.0 - 100 °C |
4.61 μin/in-°F @Temperature 104 - 212 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) |
127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) |
110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 124 °C | 255 °F | B/50; ISO R306 |
中山市沙泊塑料有限公司:主要經營各種工程塑膠原料(新料和改性料),包括: ABS、LCP、PBT、PPS、TPE、TPU、PA6、PA66、PET、POM、PMMA、PC、PC/ABS、PC/PBT,等改性產品均符合SGS檢測報告。
業務部:李厚佳
Email:ppslcp@163.com
http://www.shabosl.com/
Tel:18219005688:李生
業務部:李厚佳
Email:ppslcp@163.com
http://www.shabosl.com/
Tel:18219005688:李生
Users viewing this material also viewed the following:
Samsung Cheil Industries Infino? WP-1089 PC/ABS, Unreinforced
Samsung Cheil Industries Infino? WP-1041G PC/ABS, Unreinforced Metal Plating Grade
Mitsubishi Xantar? C CM 206 Polycarbonate/ABS Blend
Samsung Cheil Industries Infino? WP-1098 PC/ABS, Unreinforced
Samsung Cheil Industries Infino? WP-1041 PC/ABS, Unreinforced Metal Plating Grade