點擊圖片查看大圖| NYLON 66 復合材料特性及應用 | |||||||||
| NYLON66復合材料 | NYLON66 原料一般射出級 | NYLON66超韌型 | NYLON66 表面改良 | NYLON66 防火原料型 | 特殊NYLON 66低吸濕高剛性型 | 特殊NYLON 66低吸濕高剛性型、超耐動 | |||
| 物性Properties | 單位Unit | 品名Grade規范ASTM | N21A 4N-C | N21R 74N-B | N41MF 404N-C | N27A 1N-P | R63G 584B-P | N11G 602N-A | |
| 抗張強度Tensile Strength | Kg/cm2 | D-638 | 800 | 450 | 650 | 800 | 1200 | 2400 | |
| 抗張模數Tensile Modulus | Kg/cm2 | D-638 | 189800 | ||||||
| 伸長率Elongation | % | D-638 | 55 | 40 | 2.5 | 3.5 | 1.5 | 2.3 | |
| 抗折強度Flexural Strength | Kg/cm2 | D-790 | 1000 | 600 | 1100 | 1100 | 1900 | 3500 | |
| 抗折模數Flexural Modulus | Kg/cm2 | D-790 | 28000 | 16000 | 46000 | 30000 | 120000 | 172400 | |
| 動擊強度Izod | kg-cm/cm | RT | D-256 | 5 | 80 | 3.5 | 7 | 5 | 19.5 |
| -40℃ | 16 | ||||||||
| 硬度Hardness | Rockwell R | D-785 | 118 | 107 | 117 | 118 | 195 | 120 | |
| 熱變形溫度H D T | ℃ | 0.455Mpa | D-648 | 210 | 120 | 200 | |||
| 1.82Mpa | 66 | 72 | 215 | ||||||
| 灰份Filler Content | % | D-2584 | 40 | 58 | 60 | ||||
| 比重Specific Gravity | D-792 | 1.1 | 1.06 | 1.47 | 1.16 | 1.65 | 1.7 | ||
| 模收縮率Mold Shrinkage | cm/cm | D-955 | 0.012-0.018 | 1.5-2.0 | 1.2-1.4 | 1.0-1.3 | 0.1-0.2 | 0.05-0.1 | |
| 特性:1.具高機械強度 | 成型條件: | ||||||||
| 2.耐韌及耐動擊性特優 | 1.干燥溫度時間100℃/3HRS | ||||||||
| 3.電氣特性佳 | 2.成型溫度:260-290℃ | ||||||||
| 4.耐化學藥品性佳 | 3.模具溫度:70-100℃ | ||||||||
| 5.耐磨擦性佳 | |||||||||
| 備注:以上數值系參考ASTM試驗方法所測得,僅供選擇用途品級之參考. | |||||||||