| PC LV-2250Y 日本帝人化成公司 物性數據 |
①原料描述部分
| 規格級別： | --- | 外觀顏色： | --- |
| 用途概述： | --- | ||
| 備注說明： | 類型：冰色、易脫模型 | ||
②原料技術數據
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | ||||||||||||||||
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.20 | % | |||||||||||||||
| 物理性能 | 比重 | --- | JIS K-7112 | 1.20 | --- | |||||||||||||||
| 透光率 | 3mm thick | ASTM D-1003 | 88 | --- | ||||||||||||||||
| 折射率 | --- | ASTM D-542 | 1585 | --- | ||||||||||||||||
| 阻燃性 | 0.38mm | UL 94 | V-2 | --- | ||||||||||||||||
| 機械性能 |
|
--- |
|
|
|
|||||||||||||||
| 拉伸模量 | --- | ASTM D-638 | 2120(21600) | Mpa(kgf/cm2) | ||||||||||||||||
|
--- |
|
|
|
||||||||||||||||
| 彎曲強度 | --- | ASTM D-790 | 90(915) | Mpa(kgf/cm2) | ||||||||||||||||
| 彎曲模量 | --- | ASTM D-790 | 2230(22700) | Mpa(kgf/cm2) | ||||||||||||||||
| 壓縮強度 | --- | ASTM D-695 | 76(770) | Mpa(kgf/cm2) | ||||||||||||||||
| 耐沖擊強度值 | 艾氏、帶缺口厚度3.2mm | ASTM D-256 | 880(90) | J/m(kgf?cm/cm) | ||||||||||||||||
| 耐沖擊強度值 | 艾氏、帶缺口厚度6.4mm | ASTM D-256 | 140(14) | J/m(kgf?cm/cm) | ||||||||||||||||
| 洛氏硬度 | --- | ASTM D-785 | 77 | M標度 | ||||||||||||||||
| 電氣性能 | 耐導電徑跡性（CTI） | --- | IEC 112 | 300 | V | |||||||||||||||
| 絕緣破壞強度 | 快速加壓值厚度1.6mm | ASTM D-149 | 30 | kv/mm | ||||||||||||||||
| 體積電阻率 | --- | ASTM D-257 | 3×1016 | Ω.cm | ||||||||||||||||
| 介電率 | 60Hz | ASTM D-150 | 2.95 | --- | ||||||||||||||||
| 介電率 | 106Hz | ASTM D-150 | 2.9 | --- | ||||||||||||||||
| 介電正切 | 60Hz | ASTM D-150 | 0.0004 | --- | ||||||||||||||||
| 介電正切 | 106Hz | ASTM D-150 | 0.009 | --- | ||||||||||||||||
| 耐電弧性 | --- | ASTM D-495 | 110 | sec | ||||||||||||||||
| 加工性能 |
|
--- |
|
|
|
|||||||||||||||
| 熱 性 能 | 負荷撓曲溫度 | 負荷1.813MPa(18.6kgf/cm2) | JIS K-7207 | 133 | ℃ | |||||||||||||||
| 負荷撓曲溫度 | 負荷0.451MPa(4.6kgf/cm2) | JIS K-7207 | 143 | ℃ | ||||||||||||||||
|
--- |
|
|
|
||||||||||||||||
|
|
|
|
|
||||||||||||||||