以下是BASF PA66 Ultramid A3K中英文物性表
|
BASF Ultramid? A3K PA66 (尼龍66-聚酰胺)
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質(zhì)
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
Density密度
|
1.13 g/cc
|
0.0408 lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
8.0 - 9.0 %
|
8.0 - 9.0 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸濕平衡
|
2.5 - 3.1 %
|
2.5 - 3.1 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Measurement粘度
|
150
|
150
|
Viscosity number; ISO 307
|
|
Linear Mold Shrinkage線性收縮率
|
0.0085 cm/cm
|
0.0085 in/in
|
|
|
Melt Flow熔體流動(dòng)速率
|
129.95 g/10 min
@Load 11.0 lb, Temperature 527 °F |
ISO 1133
|
|
|
Mechanical Properties力學(xué)性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
Tensile Strength, Yield屈服拉伸強(qiáng)度
|
85.0 MPa
|
12300 psi
|
50mm/min; ISO 527
|
|
Elongation at Yield屈服伸長(zhǎng)率
|
5.0 %
|
5.0 %
|
50mm/min; ISO 527
|
|
Modulus of Elasticity彈性模量
|
3.10 GPa
|
450 ksi
|
ISO 527
|
|
Flexural Modulus彎曲彈性模量
|
2.90 GPa
|
421 ksi
|
ISO 178
|
|
Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度 (ISO)
|
5.50 kJ/m2
|
2.62 ft-lb/in2
|
ISO 180/A
|
|
6.00 kJ/m2
@Temperature -30.0 °C |
2.86 ft-lb/in2
@Temperature -22.0 °F |
ISO 180/A
|
|
|
Charpy Impact Unnotched夏比缺口試樣沖擊
|
NB
|
NB
|
ISO 179/1eU
|
|
Charpy ImPAct, Notched夏比缺口沖擊
|
0.500 J/cm2
|
2.38 ft-lb/in2
|
ISO 179/1eA
|
|
0.400 J/cm2
@Temperature -30.0 °C |
1.90 ft-lb/in2
@Temperature -22.0 °F |
ISO 179/1eA
|
|
|
Electrical Properties電性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
Volume ResiSTivity體積電阻率
|
1.00e+13 ohm-cm
|
1.00e+13 ohm-cm
|
IEC 60093
|
|
Dielectric Constant介電常數(shù)
|
3.2
@Frequency 1.00e+6 Hz |
3.2
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
Dissipation Factor耗散因數(shù)
|
0.025
@Frequency 1.00e+6 Hz |
0.025
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
Comparative Tracking Index跟蹤指數(shù)
|
600 V
|
600 V
|
Test Solution A; IEC 60112
|
|
Thermal Properties熱性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
CTE, linear, Parallel to Flow線性熱膨脹系數(shù)
|
0.700 - 1.00 μm/m-°C
@Temperature 23.0 - 80.0 °C |
0.389 - 0.556 μin/in-°F
@Temperature 73.4 - 176 °F |
ISO 11359-1/-2
|
|
Specific Heat Capacity比熱容
|
1.70 J/g-°C
|
0.406 BTU/lb-°F
|
|
|
Thermal Conductivity導(dǎo)熱系數(shù)
|
0.330 W/m-K
|
2.29 BTU-in/hr-ft2-°F
|
DIN 52612
|
|
Melting Point熔點(diǎn)
|
260 °C
|
500 °F
|
DIN 53765
|
|
Maximum Service Temperature, Air使用溫度
|
210 °C
|
428 °F
|
|
|
Deflection Temperature at熱變形溫度0.46 MPa (66 psi)
|
220 °C
|
428 °F
|
ISO 75
|
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi)
|
75.0 °C
|
167 °F
|
ISO 75
|
|
Flammability, UL94阻燃等級(jí)
|
V-2
@Thickness >=0.400 mm |
V-2
@Thickness >=0.0157 in |
|
|
Processing Properties加工性能
|
Metric公制數(shù)據(jù)
|
English英制數(shù)據(jù)
|
Comments測(cè)試方法
|
|
Melt Temperature熔體溫度熔體溫度
|
280 - 300 °C
|
536 - 572 °F
|
|
|
Mold Temperature模具溫度
|
60.0 - 80.0 °C
|
140 - 176 °F
|
|
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。