以下是BASF PA66 Ultramid A3X2G5中英文物性表
|
BASF Ultramid? A3X2G5 25% Glass Filled PA66 (Dry)
The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Density密度
|
1.34 g/cc
|
0.0484 lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
5.7 - 6.3 %
|
5.7 - 6.3 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸濕平衡
|
1.2 - 1.6 %
|
1.2 - 1.6 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Test 粘度
|
140 cm3/g
|
140 cm3/g
|
Viscosity number; ISO 307
|
|
Linear Mold Shrinkage線性收縮率
|
0.0050 cm/cm
|
0.0050 in/in
|
|
|
Melt Flow熔體流動速率
|
53.6 g/10 min
@Load 11.0 lb, Temperature 527 °F |
ISO 1133
|
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Tensile Strength, Yield屈服拉伸強度
|
140 MPa
|
20300 psi
|
50mm/min; ISO 527
|
|
Elongation at Yield屈服伸長率
|
3.0 %
|
3.0 %
|
50mm/min; ISO 527
|
|
Modulus of Elasticity彈性模量
|
8.00 GPa
|
1160 ksi
|
ISO 527
|
|
Flexural Modulus彎曲彈性模量
|
7.10 GPa
|
1030 ksi
|
ISO 178
|
|
Izod Impact, Notched懸臂梁缺口沖擊強度(ISO)
|
12.0 kJ/m2
|
5.71 ft-lb/in2
|
ISO 180/A
|
|
Charpy Impact Unnotched夏比缺口試樣沖擊
|
6.50 J/cm2
|
30.9 ft-lb/in2
|
ISO 179/1eU
|
|
6.00 J/cm2
@Temperature -30.0 °C |
28.6 ft-lb/in2
@Temperature -22.0 °F |
ISO 179/1eU
|
|
|
Charpy ImPAct, Notched夏比缺口沖擊
|
1.30 J/cm2
|
6.19 ft-lb/in2
|
ISO 179/1eA
|
|
Electrical Properties電性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Volume ResiSTivity體積電阻率
|
1.00e+13 ohm-cm
|
1.00e+13 ohm-cm
|
IEC 60093
|
|
Dielectric Constant介電常數
|
3.7
@Frequency 1.00e+6 Hz |
3.7
@Frequency 1.00e+6 Hz |
IEC 60250
|
|
Dissipation Factor耗散因數
|
0.020
@Frequency 1.00e+6 Hz |
0.020
@Frequency 1.00e+6 Hz |
IEC 60250
|