點擊圖片查看大圖
韓國三星毛織Samsung Cheil Industries Infino? WP-1089 PC/ABS, Unreinforced;
| Samsung Cheil Industries Infino? WP-1089 PC/ABS, Unreinforced | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; ABS Polymer; Polycarbonate/ABS Alloy, Unreinforced; Polycarbonate (PC)
|
||
| Material Notes: |
Information provided by Samsung Cheil Industries. |
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow |
0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse |
0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
Melt Flow 
|
30 g/10 min @Load 5.00 kg, Temperature 260 °C |
30 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
|
47 g/10 min @Load 10.0 kg, Temperature 250 °C |
47 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 54.4 MPa | 7890 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 MPa | 7680 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 88 % | 88 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.96 GPa | 284 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 75.5 MPa | 11000 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.11 GPa | 306 ksi | 2.8 mm/min; ASTM D638 |
|
Izod Impact, Notched
|
1.96 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
3.67 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 |
|
3.92 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
7.35 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 | |
|
4.41 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
8.27 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
|
5.88 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
11.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow |
8.10 μm/m-°C @Temperature 40.0 - 100 °C |
4.50 μin/in-°F @Temperature 104 - 212 °F |
ASTM E831 |
| CTE, linear, Transverse to Flow |
8.30 μm/m-°C @Temperature 40.0 - 100 °C |
4.61 μin/in-°F @Temperature 104 - 212 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) |
130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) |
110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | B/50; ISO R306 |
中山PC,沙伯基礎PC,德國拜耳PC,日本帝人PC、Tel:18219005688:李生
運費說明：
1.支持快遞，物流和貨運，具體運費根據貨量及具體地址而定.
2.若需試機樣品，可免費提供原料試機，運輸費用由客戶先行支付。
3.一幫情況下，發貨期限為：物流快遞1-3天，貨運2-5天，若超出期限，我們將支付超期費用。
4.收到原料后,請不要急于拆除外包裝,應先仔細檢查塑膠原料的外包裝是否完好及原料型號是否與您所訂購原料型號相匹配。
5.貨物送達后,請時間檢查,發現物流過程中出現大量包裝損壞及原料外漏的，請讓物流人員出具證明并保存，并在24小時內與我們聯系。
6.本公司原料售后的注塑加工由客戶負責，如需幫助，我司工程部將竭盡所能與您共同協商處理。
Users viewing this material also viewed the following:
Bayer MaterialScience Bayblend? T85 XF Polycarbonate + ABS
Samsung Cheil Industries Infino? WP-1069 PC/ABS, Unreinforced
Samsung Cheil Industries Infino? WP-1098 PC/ABS, Unreinforced
Bayer MaterialScience Makrolon? 2407 Polycarbonate, Injection Grade
Bayer MaterialScience Bayblend? T85 Polycarbonate + ABS